Makuuchi, K.; Hagiwara, M. published an article in 1984, the title of the article was Radiation vulcanization of natural rubber latex with polyfunctional monomers – II.Reference of 2,2-Dimethylpropane-1,3-diyl bis(2-methylacrylate) And the article contains the following content:
Natural rubber latexes were vulcanized by γ-rays with 2 polyfunctional monomers, neopentyl glycol diacrylate (I) [2223-82-7] and neopentyl glycol dimethacrylate (II) [1985-51-9]. In comparison with I, II was more soluble in rubber particles, but it was less effective as an accelerating agent for the vulcanization because of the smaller rate of polymerization On the other hand, the colloidal stability of the latex containing I was low because it was localized on the surface of rubber particles due to its poor solubility in the particles. The solubility of I was improved by adding I with solvents. The maximum tensile strength of the irradiated latex film was 350 kg/cm2 at 3 Mrad. The experimental process involved the reaction of 2,2-Dimethylpropane-1,3-diyl bis(2-methylacrylate)(cas: 1985-51-9).Reference of 2,2-Dimethylpropane-1,3-diyl bis(2-methylacrylate)
The Article related to natural rubber diacrylate vulcanization accelerator, dimethacrylate vulcanization accelerator natural rubber, Synthetic Elastomers and Natural Rubber: Vulcanization, Curing, and Crosslinking and other aspects.Reference of 2,2-Dimethylpropane-1,3-diyl bis(2-methylacrylate)
Referemce:
Ester – Wikipedia,
Ester – an overview | ScienceDirect Topics