Hu, Siwei; Huang, Biwu; Chen, Weiqing published the artcile< Synthesis of 1,1,3,3,5,5-hexamethyl-1,5-bis[(3-ethyl-3-methoxyoxetane)propyl]trisiloxane and Research on Its UV-curing Performance>, Quality Control of 112-63-0, the main research area is methoxyoxetane propyl trisiloxane preparation epoxy UV curing mech property.
A compound, 3-ethyl-3-hydroxymethyloxetane (EHO), was synthesized with di-Et carbonate and trihydroxypropane as raw materials, 3-ethyl-3-allylmethoxy oxetane (EAMO) was synthesized with EHO and allyl bromide, and 1,1,3,3,5,5-hexamethyl-1,5-bis[(3-ethyl-3-methoxyoxetane)propyl]trisiloxane (HMBEMOPTS) was synthesized with EAMO and 1,1,3,3,5,5-hexamethyltrisiloxane (HMTS). HMBEMOPTS is a novel UV-curable oligomer. The test of photo-DSC shows the photosensitivity of HMBEMOPTS is better than the ordinary oxetane, 3-ethyl-3-[(3-ethyloxetan-3-yl)methoxymethyl]oxetane. HMBEMOPTS was mixed with bisphenol A type epoxy resin E-51 to prepare a cationic UV-curable system, and triarylsulfonium hexafluoroantimonate (UV-6976) was used as a cationic photoinitiator. The mech. tests of coating films prove that when the mass fraction of HMBEMOPTS is 50%, the mech. properties of the curing system are the best. The impact strength of the UV-curable films is measured to be 40 kg-cm and the flexibility is 2 mm; the tensile strength and flexural strength of the prepared specimens are 20.74 MPa and 13.43 MPa, resp. The exptl. results show that HMBEMOPTS can effectively improve photosensitivity and flexibility of the photosensitive resin.
Journal of Wuhan University of Technology, Materials Science Edition published new progress about Bending strength. 112-63-0 belongs to class esters-buliding-blocks, and the molecular formula is C19H34O2, Quality Control of 112-63-0.
Referemce:
Ester – Wikipedia,
Ester – an overview | ScienceDirect Topics